Analysis of changes in the physical and mechanical parameters of yarn in various industries

Research was carried out to study the quality indicators of yarn. For this purpose, yarns were obtained under laboratory conditions from fibers of currently zoned varieties and varieties under trial, and their quality indicators were determined using modern equipment. The results show that, compared with yarn from cotton fiber of the industrial variety S-9085, yarns from the industrial varieties KK-3565 and KK-3523 had, respectively, 11.6% and 17.1% lower strength, 1.1% and 5.7% lower specific breaking strength, 7.1% and 3.1% higher coefficient of variation of strength, 9.9% and 9.0% higher elongation at break, and 2.7% and 21.2% higher coefficient of variation of elongation at break. It follows that the physical and mechanical properties of yarn from S-9085 fiber have been proven superior to those of yarn from other industrial varieties. To produce high-quality yarn, which is in high demand, spinning mills should above all choose the fiber composition correctly.

Проведены научно-исследовательские работы по изучению показателей качества пряжи. Для этого в лабораторных условиях из волокон районированных и проходящих испытания в настоящее время сортов получена пряжа, показатели качества которой определены с помощью современного оборудования. Результаты исследования показывают, что по сравнению с показателями пряжи из хлопкового волокна промышленного сорта С-9085 у пряжи из хлопкового волокна промышленных сортов КК-3565 и КК-3523 прочность снизилась соответственно на 11,6% и 17,1%, удельная разрывная нагрузка — на 1,1% и 5,7%, квадратическая неровнота по прочности возросла на 7,1% и 3,1%, удлинение при разрыве — на 9,9% и 9,0%, а квадратическая неровнота по удлинению при разрыве — на 2,7% и 21,2%. Отсюда следует вывод: доказано превосходство физико-механических свойств пряжи из хлопкового волокна промышленного сорта С-9085 над показателями пряжи из волокна других промышленных сортов. На прядильных предприятиях при производстве качественной пряжи, пользующейся высоким спросом, целесообразно прежде всего правильно подбирать волокнистый состав.

Ipning sifat ko‘rsatkichlarini o‘rganish bo‘yicha ilmiy-tadqiqot ishlari olib borildi. Buning uchun laboratoriya sharoitida hozirda rayonlashtirilgan va sinovdan o‘tkazilayotgan tolalardan iplar olindi hamda ularning sifat ko‘rsatkichlari zamonaviy uskunalar yordamida aniqlandi. Ilmiy tadqiqot natijalari shuni ko‘rsatadiki, S-9085 sanoat navli paxta tolasidan olingan iplar ko‘rsatkichlariga taqqoslaganda, KK-3565 va KK-3523 sanoat navli paxta tolasidan olingan iplarning pishiqligi mos ravishda 11,6% va 17,1% ga, solishtirma uzilish pishiqligi 1,1% va 5,7% ga kamaygan, pishiqlik bo‘yicha kvadratik notekisligi 7,1% va 3,1% ga, uzilishdagi uzayishi 9,9% va 9,0% ga, uzilishdagi uzayish bo‘yicha kvadratik notekisligi esa 2,7% va 21,2% ga oshgan. Bundan xulosa qilish mumkinki, S-9085 sanoat navli paxta tolasidan olingan iplarning fizik-mexanik xususiyatlari boshqa sanoat navli paxta tolasidan olingan iplar ko‘rsatkichlariga nisbatan yuqori ekani isbotlandi. Yigiruv korxonalarida talab yuqori bo‘lgan sifatli iplarni ishlab chiqarishda, eng avvalo, tola tarkibini to‘g‘ri tanlash maqsadga muvofiqdir.