Feasibility of obtaining transparent low-melting glass based on the lead–silica system

This article investigates the feasibility of obtaining transparent low-melting glasses based on the lead oxide–silicon dioxide system. Glass formation processes were studied using differential thermal analysis of batches of different compositions. As a result of the study, a composition of 80 percent lead oxide and 20 percent silicon dioxide was found to be optimal. The refractive index, density, coefficient of thermal expansion, softening temperature and chemical durability of the glasses obtained were determined. The possibility of adding up to 30 percent glass cullet to the batch was also substantiated.

В данной статье исследованы возможности получения прозрачных легкоплавких стёкол на основе системы оксид свинца – диоксид кремния. С помощью дифференциального термического анализа шихт различного состава изучены процессы стеклообразования. В результате исследования оптимальным признан состав из 80 % оксида свинца и 20 % диоксида кремния. Определены показатель преломления, плотность, коэффициент термического расширения, температура размягчения и химическая стойкость полученных стёкол. Кроме того, обоснована возможность введения в состав шихты до 30 % стеклобоя.

Ushbu maqolada qo‘rg‘oshin oksidi – kremniy dioksidi sistemasi asosida past haroratda pishuvchi shaffof shishalar olish imkoniyatlari tadqiq etilgan. Turli tarkibdagi shixtalarning differensial termik tahlili asosida shisha hosil bo‘lish jarayonlari o‘rganildi. Tadqiqot natijasida 80 foiz qo‘rg‘oshin oksidi va 20 foiz kremniy dioksidi tarkibi optimal deb topildi. Olingan shishalarning nur sindirish ko‘rsatkichi, zichligi, issiqlikdan kengayish koeffitsiyenti, yumshalish harorati va kimyoviy barqarorligi aniqlandi. Shuningdek, shixta tarkibiga 30 foizgacha shisha chiqindilarini qo‘shish imkoniyati asoslandi.